DATE | HS_CODE | Product Description | Trademark | Country | Net Weight | Statistical Cost | Place | Shipper Name | Consignee Name |
---|
2017-11-01 | 7901121000 | Zinc metal ingots UMC Contact MARK - 21000KG. PARTY â„–42 - 21000,0 CG (19 PACKETS / 988 pigs) HIM.SOSTAV,%: ZINC - 99.9875 PB - CADMIUM 0.008 - 0.0013 IRON - COPPER 0.0014 - 0.0008 Tin - 0.001 TOTAL IMPURITIES. - 0.0125. Goods are packed in packets | AMMC | UKRAINE | 21000 | 66941,9 | DNIEPER | ***** | ***** |
2017-11-01 | 7601208002 | ALUMINUM ALLOY SECONDARY, raw, obtained by the melting of scrap and waste of aluminum production, having an aluminum content less than 99 weight% to 1% zinc, to 0.85% magnesium:. MARK AK5M2 GOST 1583-93, cast molding of ingots Ingots ( | places without | JAPAN | 41958 | 73846,08 | PORT OF ST PETERSBURG | ***** | ***** |
2017-11-03 | 7601208002 | ALUMINUM ALLOY SECONDARY, raw, obtained by the melting of scrap and waste of aluminum production, having an aluminum content less than 99 weight% to 1% zinc, to 0.85% magnesium:. MARK AK5M2 GOST 1583-93, cast molding of ingots LIMIT | places without | JAPAN | 41940 | 73814,4 | PORT OF ST PETERSBURG | ***** | ***** |
2017-11-07 | 7901121000 | 5.2 PROPERTY According to the list â„– 11430.1765 PAHO. FOR PERSONS. 11 ZINC CO, GOST 3640-79 - 1,000 kg. Primary zinc ingots BRANDS U0. COMPOSITION: ZINC 99.975% 0.025% IMPURITIES (% PB 0.013, CADMIUM 0.004%, 0.005% IRON, COPPER 0.001%, tin 0.001%, 0.00 ALUMINUM | ABSENT | REPUBLIC OF INDIA | 1000 | 6902,17 | PORT Mumbai | ***** | ***** |
2017-11-07 | 7601208002 | ALUMINUM ALLOY SECONDARY, raw, obtained by the melting of scrap and waste of aluminum production, having an aluminum content less than 99 weight% to 1% zinc, to 0.85% magnesium, in the form of ingots:. MARK AK5M2 GOST 1583-93, tensile strength, | places without | JAPAN | 41948 | 74247,96 | PORT OF ST PETERSBURG | ***** | ***** |
2017-11-09 | 7601208002 | SECONDARY ALUMINUM ALLOYS, untreated, in the ingot MARKS AK5M2, GOST 1583-93, COMPOSITION: ALUMINUM -91.49%; COPPER -1.71%; MAGNESIUM -0.60%; SILICON -4.53% -0.56% IRON; Manganese -0.22%; Nickel -0.06%; ZINC -0.71%, -0.05% TITAN | TRADEMARK NO | THE SLOVAK REPUBLIC | 27000 | 32400 | KALININGRAD | ***** | ***** |
2017-11-14 | 7601208002 | ALUMINUM ALLOY SECONDARY, raw, obtained by the melting of scrap and waste of aluminum production, having an aluminum content less than 99 weight% to 1% zinc, to 0.85% magnesium, in the form of ingots:. MARK AK5M2 GOST 1583-93, tensile strength, | places without | JAPAN | 41982 | 74308,14 | PORT OF ST PETERSBURG | ***** | ***** |
2017-11-15 | 7901121000 | Zinc metal ingots UMC Contact MARK - 21000KG. PARTY â„–65 - 21000,0 CG (19 PACKETS / 988 pigs) HIM.SOSTAV,%: ZINC - 99.9855 PB - CADMIUM 0.009 - 0.0023 IRON - COPPER 0.0015 - 0.0007 Tin - 0.001 TOTAL IMPURITIES. - 0.0145. Goods are packed in packets | AMMC | UKRAINE | 21000 | 66864,55 | DNIEPER | ***** | ***** |
2017-11-16 | 7601208002 | ALUMINUM ALLOY SECONDARY, raw, obtained by the melting of scrap and waste of aluminum production, having an aluminum content less than 99 weight% to 1% zinc, to 0.85% magnesium:. MARK AK5M2 GOST 1583-93, cast molding of ingots LIMIT | places without | JAPAN | 41780 | 73532,8 | PORT OF ST PETERSBURG | ***** | ***** |
2017-11-17 | 7601208002 | ALUMINUM ALLOY SECONDARY, raw, obtained by the melting of scrap and waste of aluminum production, having an aluminum content less than 99 weight% to 1% zinc, up to 0.5% Magnesium:. MARK AK5M2 GOST 1583-93, casting in the form of ingots, the tensile strength | places without | JAPAN | 21000 | 37380 | PORT OF ST PETERSBURG | ***** | ***** |